RED OXIDE PRIMER, GENERAL PURPOSE
|
PRODUCT NUMBER |
909 |
|
|
TYPE |
Lower cost rust prevention primer based on alkyd resin and special resin with red oxide pigment. |
|
|
USES |
Used for steel structures and engineering for a large quantity use. |
|
|
CHARACTERISTICS |
1. Very fast drying. 2. Very good adhesion. 3. Very good resistance to water and weather. 4. Relatively low cost. |
|
|
FINISH |
Flat |
|
|
COLOR |
Red |
|
|
HIDING POWER |
Above 12.5 m2/L |
|
|
MASS DENSITY |
Above 1.3 Kg/L |
|
|
VISCOSITY |
70~90 KU (25 |
|
|
DRYING TIME |
Set-to-touch 30 minutes Dry hard 2 hrs.
(25 |
|
|
OPTIMUM FILM THICKNESS |
Wet 90 microns Dry 40 microns |
|
|
THEORETICAL COVERAGE |
42.0 |
|
|
OVERCOATING INTERVALS |
Min. 6 hrs. |
|
|
NON-VOLATILE CONTENT |
Above 65% |
|
| THINNER | No.805
Paint Thinner  OM-07
|
|
| THINNING RATE | 5~10%  cleaning for tools not
included |
|
| PRECEDING COATS | No.905 High Red Lead Primer OP-91 No.906 Red Lead Primer OP-92 No.907 Zinc Chromate Primer OP-93 No.908 Wash Primer SP-01/SP-02 |
|
℃) 
℃)
m2/Gal
11.1 
m2/L
8.5 m2/Kg |
SUBSEQUENT COATS |
Rainbow Ready-Mixed Paint |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Spray, Brush |
|
NOTE |
1. Before application, stir paint evenly, and when paint is too thick, thinner within specified quantity can be added. 2. Adhered moisture, grease, dirt, damaged or loose old paint and corrosive salts on substrate must be cleaned thoroughly. 3. Avoid applying the paint in
rainy, humid weather or substrate temperature excessively high to 40 4. Avoid applying to
insufficient drying of previous paint coat. |
or low to 10
. 
|
|
|
|
 |
|
|
|