RAINBOW C.R. LZI PRIMER
| PRODUCT NUMBER | No.1449(RP-64) |
| TYPE | Anti-corrosive paint based on Chlorinated Rubber with red lead, zinc chromate and iron oxide pigment. |
| USES | Anti-corrosive under coat for steel structure and machine. |
| CHARACTERISTICS | 1.
Very fast drying and good adhesion. 2. Very good resistance to oil and seawater. 3. Very good rust preventive property.(salt water(5%) test for 120 hrs. 4. Easy application. |
| APPLICATION METHOD | Brush, Roller, Airless Spray. |
| COLOR | Red oxide |
| FINISH | Flat |
| HOLDING POWER | Above 12.5 m2/L |
| SPECIFIC GRAVITY | Above 1.3 kg/L |
| VISCOSITY | 70 ~ 100 KU (25 ℃) |
| BANDING TEST | 6m/m |
| SALT WATER TEST | NaCl(3%) for 144 hrs. |
DRYING
TIME (25 ℃) | Set-to-touch 1 hr. Dry hard 3 hrs. |
| OVERCOATING INTERVALS | Min. 4 hrs. (25℃ ) |
| OPTIMUM FILM THICKNESS | Wet 90 microns (3.6 mil) Dry 40 microns (1.6 mil) |
| VOLUME SOLIDS | Above 62% |
| THEORETICAL COVERAGE | 11.1 m2/L
8.5 m2 /KG 42 m2/GL |
| THINNER | RP-71 PCR Thinner |
| THINNING RATE | 5 - 15 % (by wt.) |
| PRECEDING COATS | No.908 Wash Primer |
| SUBSEQUENT COATS | Chlorinated Rubber or Alkyd topcoats. |
| NOTE | 1.
Before application, stir paint evenly. When paint is too thick, thinner can be added within specified quantity 2. Moisture, grease, rust, dirt and loose paints film on substrate must be removed, so are the corrosive salt particles. As a result, paint performance can be ensured. 3 Application should avoid the following environment: rainy day; substrate is damp by dew; temperature is above 40℃  or below 10℃ . 4. Subsequent coat has to wait until paint films of preceding coat completely dry off. |
|
|
|
|
 |
|
|
|