EPOXY WATER TANK COATING |
|
|
PRODUCT NUMBER |
1017 (EP-07) |
|
TYPE |
A two-pack, high-build water tank paint based on epoxy resin and special hardener with water resistant pigment. |
|
USES |
Used for potable water and fresh water tanks, also suitable for cargo hold, crude oil tanks and ballast tanks etc. |
|
CHARACTERISTICS |
1. High build (100µ film can be obtained by one coat spray.) 2. Tough and hard film, outstanding abrasion resistance. 3. Excellent resistance to water, oils and chemicals. 4. Excellent protection against corrosion. 5. No contamination to fresh water. |
|
FINISH |
Gloss |
|
COLOR |
White, grey or desired colors |
|
MASS DENSITY |
Above 1.25 Kg/L (mixture) |
|
VISCOSITY |
90~110 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 2 hrs. Dry hard 10 hrs. Fully cured 7 days (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 192 microns Dry 100 microns |
|
THEORETICAL COVERAGE |
19.7 ㎡/Gal 5.2 ㎡/L 4.17 ㎡/Kg |
|
OVERCOATING INTERVALS |
Min. 20 hrs. Max. 5 days (25℃) or 3 days (30℃) |
|
MIXING RATIO |
Base : hardener = 94 : 6 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 65% (mixture) |
|
POT LIFE |
8 hrs. (mixture, 20℃) |
|
HEAT RESISTANCE |
Continuous 93℃ |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) (only cleaning tools) |
|
THINNING RATE |
5~10% (by wt, cleaning tools excluded) |
|
PRECEDING COATS |
Steel: No.1006 Epoxy Zinc Rich Primer (EP-03) No.1075 Epoxy Aluminum Tripolyphosphate Primer Concrete: No.1073 Epoxy Clear Cement Primer No.1002 Epoxy Primer, white |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. The surface of cement wall or cement products must be thoroughly dried then can be applied. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. |
|
|
|
|
 |
|
|
|