EPOXY ALUMINUM TRIPOLYPHOSPHATE PRIMER
|
PRODUCT NUMBER |
1075 (EP-99) |
|
TYPE |
A two-pack, anti-corrosive paint based on epoxy resin and iron dioxide with aluminum tripolyphosphate non-pollution pigment. |
|
USES |
Used for the steel structures of boottop above, storage tank, pipeline, plant facility. |
|
CHARACTERISTICS |
1. Excellent resistance to sea water. 2. Excellent rust preventive properties. 3. Tough and hard film with very good adhesion. 4. Excellent resistance to mechanical damage. 5. Very good resistance to oils and chemicals. |
|
FINISH |
Flat |
|
COLOR |
Oxide Red, white or grey |
|
FLASH POINT |
20℃ (68 ℉) |
|
MASS DENSITY |
Above 1.3 Kg/L (mixture) |
|
VISCOSITY |
70~85 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 1 hr. Dry hard 4 hrs. Fully cured 7 days (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 100 microns Dry 45 microns |
|
THEORETICAL COVERAGE |
37.8 ㎡/Gal 10.0 ㎡/L 7.4 ㎡/Kg. |
|
OVERCOATING INTERVALS |
Min. 8 hrs. (25℃) |
|
MIXING RATIO |
Base : Hardener = 92.3 : 7.7 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 60% |
|
POT LIFE |
8 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~15% |
|
PRECEDING COATS |
No.908 Wash Primer (SP-01/02) No.1011 Inorganic Zinc Rich Primer (IZ-01) No.1006 Epoxy Zinc Rich Primer (EP-03) |
|
SUBSEQUENT COATS |
Epoxy, Vinyl, CR or PU system |
|
FOR AIRLESS SPRAY |
Tip Size Graco 319~719, 321~721 Air pressure 4~ 6 Kg/cm2 Pressure Ratio 45:1, 33:1, 28:1 for airless spray. |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller. |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly. 2. Avoid applying the paint in rainy or humid weather and particularly a wet surface must be thoroughly dried. 3. All equipment must be cleaned immediately after use. 4. When used inside tanks, sufficient ventilation must be provided. 5. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. |
|
|
|
|
 |
|
|
|