EP-12 SOLVENTLESS EPOXY ANTICORROSION PAINT

SOLVENTLESS EPOXY ANTICORROSION PAINT


PRODUCT NUMBER

EP-12

TYPE

A two-component, anticorrosion paint based on epoxy resin and special hardener with special pigment.

USES

Used for the steel structures of steel pipeline, steel frame, bridge and plant facilities etc to effectively protect substrate for a long-term.

CHARACTERISTICS

1. The paint is a solvent-free coating that can get high-build paint film to improve spray efficiency.

2. This paint has no those defects that easily produced from general high-build coatings, such as uneasy curing, sagging, blistering, cracking etc.

3. Very fast harden, especially suitable for the steel structure of continuous production

4. Excellent physical and chemical properties to improve life of substrates, and the solvent-less property meets green new trend.

FINISH

Gloss

COLOR

Gray

HIDING POWER

Above 20 ㎡/L (mixture)

MASS DENSITY

Above 1.5 Kg/L

DRYING TIME

Set-to-touch 2 hrs. (25℃)

Dry hard 4 hrs. (25℃) or 12 minutes (90℃)

SPRAY TEMPERATURE

55 ~ 60℃

OPTIMUM FILM THICKNESS

Wet 700 microns

Dry 700 microns

THEORETICAL COVERAGE

5.3 ㎡/Gal 1.4 ㎡/L 0.9 ㎡/Kg

MIXING RATIO

Base : Hardener = 2 : 1 ( by weight = by volume )

NON-VOLATILE CONTENT

Above 97%

POT LIFE

25℃: 40 minutes 60℃: 6 minutes

THINNER

No.1005 Epoxy Thinner (SP-12).

THINNING RATE

Only for cleaning tools

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

APPLICATION METHOD

Airless spray attached heat equipment

NOTE

1. Mix base and hardener according to the mixing ratio. Spray temperature was recommended to try more than 50℃, and air pressure is greater than 340 Kg/cm2 to ensure base and hardener spraying evenly.

2. Moisture, grease, sludge, dust, corrosion and salt must be thoroughly removed from substrate.

3. Avoid applying the paint in rainy weather or the relative humidity exceeded 85%, particularly, a wet surface must be thoroughly dried.

4. All equipment must be cleaned immediately after use.

5. Thickness of paint film can not exceed 1500 microns by once spray to avoid sagging.