EP-988 EPOXY HIGH SOLIDS COATING FOR ANTI-CORROSION

EPOXY HIGH SOLIDS COATING FOR ANTI-CORROSION


PRODUCT NUMBER

EP-988

TYPE

The high solids coating based on epoxy resin with anti-corrosive pigment and mica powder.

USES

Used for ship, bridges, tanks, pipelines, petrochemical plants and steel structures.

CHARACTERISTICS

1. Tough and hard film, excellent abrasion resistance.

2. Excellent anti-corrosion and water resistance.

3. Use green anticorrosion pigment in formula, both excellent inhibitory and hiding performance of corrosive protection for steel.

4. Excellent resistance to oils and chemicals.

5. Can be applied to variety types of coating, or be coated a variety types of coating, for the best maintenance coating.

6. When use high weather resistant paint, the anti-corrosion performance is especially excellent.

COLOR

Brown, Gray

FLASH POINT

Above 25℃

SPECIFIC GRAVITY

Above 1.56 Kg/L (mixture)

VISCOSITY

About 96 KU (mixture)

DRYING TIME

Set-to-touch 4 hrs. Dry hard 12 hrs. Fully cured 7days (25℃)

OPTIMUM FILM THICKNESS

Wet 108~652 microns Dry 100~600 microns

VOLUME SOLIDS

92±1﹪

THEORETICAL COVERAGE

35.2 ㎡/Gal 9.3 m3/L 5.96 m2/Kg (DFT :100 um)

OVERCOATING INTERVALS

Min. 10 hrs. Max. 7 days(top coat) 28 days(EP-988)

THINNER

Xylene or SP-12 Epoxy thinner (0~5%)

SUBSEQUENT COATS

Epoxy、Polyurethane、Fluorocarbon resin system

MIXING RATIO

Base : hardener = 77.6 : 22.4 (by weight)

POT LIFE

4 hrs. ( mixture, 25℃ )

STORAGE SHELF LIFE

Minimum 2 years under normal storage conditions.

APPLICATION METHOD

Airless Spray, Brush, Roller

FOR AIRLESS SPARY

Tip size 0.025’’ Air pressure 4 Kg/cm2 Pump ratio 45:1 or greater

NOTE

1. Mix base and hardener according to the mixing ratio and stir thoroughly.

2. Moisture, grease, sludge, dust, corrosive salt must be thoroughly cleaned from substrate.

3. Avoid applying the paint in raining weather or the relative humidity exceed 85%RH, particularly, a wet surface must be thoroughly dried.

4. All equipments must be cleaned immediately after use.

5. The coating should be stored in cool ventilated place, do not exposed to the sun in outdoor to avoid affecting the quality.

6. To increase or decrease the usage of thinner depending on the temperature of the coated surface, the temperature decreased may have to add more amount of thinner.