No.1087P EPOXY UNDER WATER PRIMER

EPOXY UNDER WATER PRIMER

PRODUCT NUMBER

No.1087P

TYPE

A two-pack corrosion preventive coating based on special epoxy resin and hardener.

USES

Used for coast and harbor facilities, or for the steel of the underwater area.

CHARACTERISTICS

1. Can easy brush to steel in water with good adhesion.

2. Brushing have good shear strength suitably, blasting steel under water have good wetting and adhesion. Coating can be cured under water, it doesn’t be washed away by seawater.

3. Hard and tough film with excellent abrasion resistance, excellent resistance to water.

4. 400 microns of dry film can be obtained by one coat brush.

APPLICATION METHOD

Brush

COLOR

Gray

FLASH POINT

Above 100℃

SPECIFIC GRAVITY

Above 2.2 Kg/L (mixture)

VISCOSITY

10000~15000 cps(25℃)

DRYING TIME

Set-to-touch 2 hrs. half dry 4 hrs.

Dry hard 6 hrs. Fully cured 7days (25℃)

OVERCOATING INTERVALS

Min. 3 hrs. Max 3 days.

OPTIMUM FILM THICKNESS

WFT: 365 (microns) DFT: 350 (microns)

THEORETICAL COVERAGE

0.8 ㎡/Kg @ 350 um

THINNER

No.1005 Epoxy Thinner (SP-12) (Only for tools cleaned)

PRECEDING COATS

No.1087 Epoxy Under Water Coating

MIXING RATIO

Base : hardener = 90 : 10 (by wt.)

POT LIFE

40 minutes (mixture, 1Kg/25℃)

ADHESION

Brush on blasting steel on water: above 30Kg/cm2

Brush on blasting steel under water: above 12Kg/cm2

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

NOTE

1. Mix base and hardener according to the mixing ratio and stir thoroughly.


2. The coating surface attach halobios easily under water, all halobios must be cleaned thoroughly when brush on the second day, or it may affect adhesion.

3. Brushing with short bristle brush have good shear strength and wetting effect under water.

4. Pot life is 40 minutes (mixture, 1Kg/25℃), mixing too much may have bad construction.