WATER-BASED INORGANIC ZINC SILICATE
|
PRODUCT NUMBER |
No.1034 |
|
TYPE |
A two-pack, inorganic zinc rich rust preventive paint based on ethyl silicate and purity zinc |
|
USES |
Long-potent rust preventive coating for ship's shell, cargo hold or steel structures of power oil refineries and pulp factories etc. |
|
CHARACTERISTICS |
1. Excellent corrosion and weather resistance. 2. Excellent heat resistance withstands up to400 ℃. 3. Excellent resistance to mechanical damage. 4. Unaffected by gas-cutting and welding. 5. Excellent resistance to oil and organic solvents. |
|
GLOSS |
Flat |
|
COLOR |
Gray |
|
WEIGHT |
2.8 kg/L (Mixer) |
|
VISCOSITY (25 ℃) |
70~85 KU (Mixer) (25 ℃) |
|
DRYING TIME (25 ℃) |
Set-to-touch 10mins. Dry hard 1.5 hrs |
|
OPTIMUM FILM THICKNESS |
75 μ（microns） |
|
OVERCOATING INTERVALS (25℃) |
Min. 24 hrs. |
|
THEORETICAL COVERAGE |
31.4 ㎡/Gal 8.3 m2/L 2.89 m2/kg |
|
MIXER RATE |
= 29 : 71 |
|
NON-VOLATILE CONTENT |
Above 75％ (Mixer) |
|
POT LIFE |
7 hrs. (Mixer, 25 ℃) |
|
382℃ |
|
|
THINNER |
Water |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush. |
| NOTE | 1. Pour the zinc dust gradually into the base
with constant stirring, and then pass through 80mesh
filter. 2. When used inside tanks, sufficient ventilation must be provided. 3. One mist coat must be applied before finish coats to avoid blistering. 4. Steel surfaces must be blast-cleaned to SIS Sa2 1/2, with moderate roughness |
|
|
|
|
 |
|
|
|